Accelerated Stress Test Method for the Assessment of Membrane Lifetime in Vanadium Redox Flow Batteries.
Journal article

Accelerated Stress Test Method for the Assessment of Membrane Lifetime in Vanadium Redox Flow Batteries.

  • Oldenburg FJ Electrochemistry Laboratory , Paul Scherrer Institut , 5232 Villigen PSI , Switzerland.
  • Ouarga A Electrochemistry Laboratory , Paul Scherrer Institut , 5232 Villigen PSI , Switzerland.
  • Schmidt TJ Electrochemistry Laboratory , Paul Scherrer Institut , 5232 Villigen PSI , Switzerland.
  • Gubler L Electrochemistry Laboratory , Paul Scherrer Institut , 5232 Villigen PSI , Switzerland.
Show more…
  • 2019-11-20
Published in:
  • ACS applied materials & interfaces. - 2019
accelerated stress test
degradation mechanism
membrane degradation
membrane lifetime
vanadium redox flow battery
English An accelerated stress test (AST) method was developed to estimate the lifetime of ion-exchange membranes in a vanadium redox flow battery. The oxidative VO2+ ions present in the charged positive electrolyte are the predominant stressor causing loss of functional groups and membrane conductivity. Membrane aging was accelerated in ex situ tests by exploiting elevated temperatures and the increased oxidative strength of Ce4+. Acceleration factors were determined on the basis of the analysis of aged radiation grafted g(S-AN) membranes. The degradation in a Ce4+ solution was found to be ∼4 times faster than in VO2+. The highest acceleration factor of ∼200 was found for the degradation with Ce4+ at 80 °C. The degradation reaction present in the accelerated stress test showed a similar activation energy of ∼50 kJ/mol in VO2+ and Ce4+ solutions, suggesting a similar reaction pathway. The applicability of the test was further evaluated with the second membrane, g(AMS-MAN). Its lifetime was estimated based on the accelerated stress test and acceleration factors previously determined for the g(S-AN) membrane and compared to the lifetime projected from an extended cycling experiment in the cell. The two values were in the same range of ∼4000 h. The proposed AST can serve as a basis for predictive modeling of membrane lifetime in vanadium redox flow batteries. The potential of the method and the limitations are discussed.